Cylindrical Powders and Propellants

M9(0) Propellant

Charge Weight Shape: 5,8 g
Type: Cylindrical Double Base
Pressure (kgf/cm²): --
Mean Velocity (m/sn): --

CBI (Tip II) Propellant

Charge Weight Shape: --
Type: Cylindrical
Pressure (kgf/cm²): Single Base
Mean Velocity (m/sn): --

155 mm M1 Propellant

Charge Weight Shape: 2600 g
Type: Cylindrical Single Base
Pressure (kgf/cm²): 1969 bar
Mean Velocity (m/sn): 374,9

155 mm M1 Propellant with 7 Perforations

Charge Weight Shape: 6200 g
Type: Cylindrical with 7
Pressure (kgf/cm²): perforations Single Base
Mean Velocity (m/sn): Max. 2250 ba

155 mm M6 Propellant

Charge Weight Shape: 9560 g
Type: Cylindrical with 7 perforations
Pressure (kgf/cm²): Single Base Min. 1828 bar
Mean Velocity (m/sn): Max. 2320 bar Max. 686,1

120 mm CEP-2 Propellant

Charge Weight Shape: --
Type: Cylindrical with 7
Pressure (kgf/cm²): perforations Double Base
Mean Velocity (m/sn): 686 bar

106 mm M26 Propellant

Charge Weight Shape: 3650 g
Type: Cylindrical with 7 perforations
Pressure (kgf/cm²): Double Base Max. 781 bar
Mean Velocity (m/sn):

105 mm M1 Propellant (PANTER)

Charge Weight Shape: 2850 g
Type: Cylindrical with 7 perforations
Pressure (kgf/cm²): Single Base Max. 2230 bar
Mean Velocity (m/sn):

105 mm M30 Propellant

Charge Weight Shape: 5800 g
Type: Cylindrical with 7 perforations
Pressure (kgf/cm²): Triple Base
Mean Velocity (m/sn): Max. 4254 bar

40 mm M9 Propellant

Charge Weight Shape: 0.45 g
Type: Cylindrical Double Base
Pressure (kgf/cm²): 3700 ± 200 bar
Mean Velocity (m/sn): 75 ± 5

12.7 mm Cartridge Powder

Charge Weight Shape: --
Type: Cylindrical with 7
Pressure (kgf/cm²): perforations Double Base
Mean Velocity (m/sn): 686 bar

Smokeless Shutgun (Flake)

Charge Weight Shape: --
Type: Cylindrical Single Base
Pressure (kgf/cm²): 450-650 bar
Mean Velocity (m/sn): Min. 350

7.62 mm Nato Powder

Charge Weight Shape: 2,85 g
Type: Cylindrical Double Base
Pressure (kgf/cm²): 3375 bar
Mean Velocity (m/sn): 838±4,6

7.62 mm (M82) Blank Powder

Charge Weight Shape: 0,74 g
Type: Cylindrical Single Base
Pressure (kgf/cm²): Max. 2550 bar
Mean Velocity (m/sn): --

Ball Powder (5.56 mm x 45)

Charge Weight Shape: Spherical
Type: Double Base
Pressure (kgf/cm²): Max. 3654 Bar
Mean Velocity (m/sn): 914.4 ± 6.1 m/s
Standard deviation: Max. 7.6 M/S

Ball Powder (7.62 mm x 51)

Charge Weight Shape: Spherical
Type: Double base
Pressure (kgf/cm²): Max. 3516 bar
Mean Velocity (m/sn): 833±4,6 m/s
Standard deviation: Max. 6,1 m/s

7.62mm x 39 Kalashnikov Ball Powder

Charge Weight Shape: Spherical
Type: Double Base
Pressure (kgf/cm²): Max. 2850 bar
Mean Velocity (m/sn): 710±15 m/s
Standard deviation: --

Ball Powder (9 mm x 19)

Shape: Spherical
Type: Double base
Pressure (kgf/cm²): Mean Piezo 6203: Max. 2150 bar
Velocity (m/sn): Piezo 6215: Max. 2350 bar
Standard deviation: 375±7,6 Max. 6,1 m/s

Ball Powder (12.7 mm x 99)

Shape: Spherical
Type: Double Base
Pressure (kgf/cm²): KIAG 6215: Max. 4344 bar
Mean Velocity (m/sn): KIAG 6215: 885±4,6 m/s
Standard deviation: Max. 9,1 m/s

TNT / (Trinitrotoluene)

Appearence: From light to dark yellow in color, flake
Water Content: % 0.1 max.
Acidity (H2SO4): % 0.02 max.
Insoluble Matter: % 0.05 max.
Sodium(Na) Compounds: % 0.001 max.
Flake size: Average thickness less than 0.63 mm, individual thickness less than 1.02 mm
Solidification Point: 80,20 °C min.

RDX (Hexogen)

Color and Appearence: From light to dark yellow in color, flake
Melting Point, °C, min.: % 0.1 max.
Acetone InsolubleMatter,: % 0.02 max.
% (m/m), max.: No
Ash Content,% (m/m), max.: % 0.05 max.
Acidity, %(m/m),max.: % 0.001 max.
HMX Content , %(m/m): Average thickness less than 0.63 mm,
Inorganic insoluble %(m/m): individual thickness less than 1.02 mm
Impact Sensitivity cm (min.): 80,20 °C min.
Holston impact method:
Impact Sensitivity cm (min.):
ERL,Type 12, 2.5 kg:
Granulation:

HMX (Octogen)

Color and Appearence: White crystal min.
HMX Content, % (m/m): 98
RDX Content,% (m/m): max. 2
Acetone Insoluble Matter, % (m/m): max. 0.05
Melting Point, °C,: min. 277
Ash Content, % (m/m): max. 0.03
Acidity, % (m/m): max. 0.02
Inorganic Insoluble %(m/m): max. 0,03
Impact Sensitivity cm (min.): min. 26
Impact Sensitivity cm (min.): min. 17
Granulation: Large range

nc (NITROCELLULOSE)

Nitrogen Content (%): 13.1±0.1
Viscosity (cp): 28± 6
Insoluble matter in Acetone (%): Max. 0.4
B&G stability test at 132 °C (ml/gr): Max. 2.2
Ether – Alcohol solubility (%): 33 ± 5
Fineness (ml): Max. 84
Stability test at 134.5 °C: Min. 30
Moisture content (%): --